Magnesium Oxide Doped Lithium Niobate Crystals
(MgOiNbO3)
Compared with LiNbO3 crystal, MgOiNbO3 crystal exhibits its particular advantages for NCPM frequency doubling (SHG) of Ndasers, mixing (SFG) and optical parametric oscillators (OPOs). The SHG efficiencies
of over 65% for pulsed Nd:YAG lasers and 45% for cw Nd:YAG lasers have been achieved in MgOiNbO3 crystals, respectively. MgOiNbO3 is also a good crystal for optical parametric oscillators (OPOs) and amplifiers (OPAs), quasi-phase-matched doublers and integrated waveguide.

MgOiNbO3 has similar effective nonlinear coefficients to pure LiNbO3. Its Sellmeier equations (for MgO dopant 7 mol%) are:

         n2o (l) = 4.8762+0.11554/(l2 - 0.04674)-0.033119´ l2      ( l in mm)

          n2o (l) = 4.5469+0.094779/(l2 - 0.04439)-0.026721´l2


--------------------------------------------------------------------------------

Other Ions Doped Lithium Niobate Crystals

ZnOiNbO3 crystal has the advantages of high damage threshold, non-critical phase-matching and good physical and chemical properties like MgOiNbO3. It has better optical quality and lower absorption loss than MgOiNbO3. Therefore, it is another candidate for frequency doublers  mixers, OPOs  OPAs, and quasi-phase-matched doublers and integrated optics.

FeiNbO3 crystals is a kind of excellent photorefractive crystals for phase conjugations and holographic gratings and recording. Please refer to the photorefractive crystals for details.